Secondary Vulcanization

Basic Info.

Origin	Anhui Bengbu
HS Code	39100000
Production Capacity	1000tons

Product Description

Post cured free high bite force liquid silicone rubber series of IOTA M6040K DescriptionIOTA M6040K A/B series product is a high bite force liquid silicone rubber free of post cured.FeaturesTwo-component, 1:1 mixing ratioExcellent mold releaseVOC less than 0.5%Fast thermal curingExcellent mechanical propertiesComply with BfR, FDA, ROHS requirementsApplicationBaby careFood contactSealing ringOther injection products, etc.Curing: The curing time of addition products is largely temperature dependent.

Temperature	Curing time, 2mm thickness
130ºC	90 S
150ºC	45 S

Notes:The series of IOTA M6040K A/B is a platinum catalyzed product, which is in component A, pay strict attention when using to avoid catalyst poisoning. Only same batch of components A and B could be mixed together. In order to ensure the best fluidity and evenly of materials, materials must be fully mixed before transferred to containers. Technical data

Properties	M6040K	M6050K	M6060K
Uncured products
Component A
Color	Transparent
Density 23ºC,g/cm3	1.12	1.12	1.12
Viscosity 23ºC, 10S-1	320Pa.s	350 Pa.s	350Pa.s
Component B
Color	Transparent
Density 23ºC, g/cm3	1.12	1.12	1.12
Viscosity 23ºC, 10S-1	280Pa.s	300 Pa.s	300Pa.s
Product data (A+B mix)
Mixing ratio (weight)	1:1
Viscosity 23ºC, 10S-1	300 Pa.s	350 Pa.s	350Pa.s
Curing time	See curing conditions
Product data (after curing)	(125±2ºC,cured for 5min)
Color	Transparent
Density 23ºC,g/cm3	1.11	1.12	1.12
Hardness	40	50	60
Tensile Strength	9 Mpa	10 Mpa	9 Mpa
Elongation	580 %	550 %	450 %
Tear strength	35KN/m	40 KN/m	38KN/m

Packaging & storage A component 200 Kg/drum,B component 200 Kg/dum. Store under 23ºC to avoid exposure to rain and sunlight. Shelf life: 12 months, unopened condition.